Development of an antimicrobial resin—A pilot study
Dental Materials. Volume 27, Issue 4, Pages 322-328 (April 2011)
To demonstrate that silver nanoparticles (AgNPs) could be synthesized in situ in acrylic dental resins.
Methods: Light-cure (LC; bisphenol A glycidyl methacrylate, tetraethyleneglycol dimethacrylate, bisphenol A ethoxylate dimethacrylate blend) and chemical-cure systems (CC; orthodontic denture resin) were used to synthesize AgNPs using different concentrations of Ag benzoate (AgBz).
Results: Rockwell hardness for LC resins showed that resins could be cured with up to 0.15% AgBz, while the hardness of CC resins were unaffected in the concentrations tested. UV–Vis spectroscopy and transmission electron microscopy confirmed the presence of AgNPs in both LC and CC resins. Generally, CC resins had better distribution of and much smaller AgNPs as compared to LC resins overall. In some samples, especially in LC resins, nanoclusters were visible. An in vitro release study over four-weeks showed that CC resins released the most Ag+ ions, with release detected in all samples. However, LC resins only released Ag+ ions when AgBz concentration was greater than 0.1% (w/w). AgNP-loaded CC resins made with 0.2 and 0.5% (w/w) AgBz were tested for antibacterial activity in vitro against Streptococcus mutans, and results showed 52.4% and a 97.5% bacterial inhibition, respectively. Further work is now warranted to test mechanical properties and to optimize the initiator system to produce commercially useful dental and medical resins.
Significance: Success in this work could lead to a series of antimicrobial medical and dental biomaterials that can prevent secondary caries and infection of implants.
Sign up for our Monthly Email Update summarizing all new posts to Esstechinc.com, CLICK HERE.
Friday, September 10th, 2010
Effects of adhesive, base and diluent monomers on water sorption and conversion of experimental resins
Sabine H. Dickens, Glenn M. Flaim, Cynthia J.E. Floyd
Dental Materials Volume 26, Issue 7, Pages 675-681 (July 2010)
Objectives: To establish the relationship of resin composition and resin hydrophilicity (indicated by solubility parameters and logP) to water sorption (WS), solubility, and degree of double bond conversion (DC) of resin mixtures designed for adhesive restoratives by varying the concentration of pyromellitic glycerol dimethacrylate (PMGDM) and various co-monomers.
Methods: Sixteen resin mixtures were prepared with (30–70) mass fraction % PMGDM. At given PMGDM concentrations there were up to five compositions with increasing logP. Polymer disks (13mm×0.7mm) were exposed to 96% relative humidity (RH) to determine water sorption in humid atmosphere (WSH) and subsequently immersed in water for immersion water sorption (WSI) and solubility. DC was assessed by near infrared spectroscopy.
Results: WSI was somewhat higher than WSH, which ranged from (2.1 to 5.3) mass fraction %. Both data were positively correlated to PMGDM concentrations [Pearson correlation, p<0.02; R2=0.74, 0.73 (WSI)] and solubility (R2=0.64), but not to logP. When grouped by structural similarities, i.e., base resins with bisphenol A core (Group B), Group O containing diluent monomers, or Group U containing urethane dimethacrylate, WS within each group was inversely correlated to logP with R2=0.98, 0.81, 0.95, and WS/solubility correlation improved with R2=0.88, 0.92 and 0.75, respectively. Solubility ranging from 0.3% to 2.3% was inversely related to DC (r=−0.872). Conversion ranging from 41% to 81% was lower for resins with high base monomer concentrations and highest in mixtures with UDMA.
Significance: LogP was a good predictor of WS after grouping the resins according to functional, compositional and structural similarities. WS and conversion were reasonably well predicted from Hoy’s solubility parameters and other physical resin properties.
Tuesday, July 27th, 2010
Degree of conversion and color stability of the light curing resin with new photoinitiator systems
Dong-Hoon Shin, H. Ralph Rawls
Dental Materials, August 2009 (Vol. 25, Issue 8, Pages 1030-1038)
Objectives: This study investigated p-octyloxy-phenyl-phenyl iodonium hexafluoroantimonate (OPPI) as a photoinitiator, in combination with camphorquinone/amine photoinitiation systems, for use with di(meth)acrylate-based composite resins. The investigation determined if the inclusion of OPPI improved degree and rate of conversion, initial color and color stability of a representative composite resin dental material.
Methods: Camphorquinone (CQ) and OPPI were combined in various proportions with the amine co-initiator 2-dimethylaminoethyl methacrylate (DMAEMA) and used at two levels in which CQ+OPPI+DMAEMA=1wt.% or 3wt.% to photoinitiate a BisGMA/BisEMA/TEGDMA (37.5:37.5:25wt.%) monomer blend. Monomer mixture (GTE) was made by mixing 37.5wt.% BISGMA (lot # 568-21-07, ESSTECH, Essington, PA), 37.5wt.% BISEMA (lot # 474-32-02, ESSTECH), and 25wt.% TEGDMA (lot # 597-23-02, ESSTECH). A total of eight groups (four groups for each level of total photoinitiator, 1% and 3%) were tested according to the following proportion of components in the photoinitiator system: Each monomer was polymerized using a quartz-halogen curing unit (Demetron 400, Demetron Research Corp., Danbury, CT) with an intensity of 400mW/cm2 for 5s, 20s, 40s, 60s, 300s and their conversion levels (DC) were determined at each exposure time using a Fourier transform infrared spectrophotometer (FTIR). To examine color stability, experimental composite resins were made by mixing 3.2% silanated barium glass (78wt.%, average filler size; 1μm) with each monomer system, except both CQ only group and 1% CO group, which were found to cure insufficiently to be able to prepare useful specimens. Disk-shaped samples (10mm in diameter and 1.5mm in thickness) were made and stored under the conditions of dry or saline solution at room temperature (25°C) or 60°C water bath. Each CIELAB scale was determined with a colorimeter (CHROMA METER CR-400) at the time of baseline (day after curing), 1 week, 2 weeks, and 4 weeks later.
Results: The high level (3%) photoinitiated groups exhibited greater DC than the low level (1%) groups. In the 3% group, the COA group showed the fastest and the highest DC, while in the 1% group the CA and COA groups showed the greatest DC. In the color stability test, both CA groups were darker and more yellow than the CO and COA groups. Color was more stable in composite resins containing OPPI than those containing only the CQ and amine components. The least color change (greatest color stability) was found using 25°C saline solution aging, and the most change (least color stability) occurred using 60°C dry air aging.
Significance: This study suggests that OPPI can be used to replace the amine in a given CQ/amine photoinitiator system to accelerate cure rate, increase conversion, reduce initial color and increase color stability.
Friday, May 21st, 2010
Bis-GMA co-polymerizations: Influence on conversion, flexural properties, fracture toughness and susceptibility to ethanol degradation of experimental composites
Carmem S. Pfeifer, Laura R. Silva, Yoshio Kawano, Roberto R. Braga
Dental Materials Volume 25, Issue 9, Pages 1136-1141 (September 2009)
The aim of this study was to evaluate the influence of monomer content on fracture toughness (KIc) before and after ethanol solution storage, flexural properties and degree of conversion (DC) of bisphenol A glycidyl methacrylate (Bis-GMA) co-polymers.
The 30B:70T composite presented the highest KIc value (in MPam1/2) at 24h (1.3±0.4), statistically similar to 30B:35T:35U and 30B:70U, while 30B:70E presented the lowest value (0.5±0.1). After ethanol storage, reductions in KIc ranged from 33 to 72%. The 30B:70E material presented the lowest reduction in FT and 30B:70U, the highest. DC was similar among groups (69–73%), except for 30B:70U (52±4%, p<0.001). 30B:70U and 30B:35T:35U presented the highest FS (125±21 and 122±14MPa, respectively), statistically different from 30B:70T or 30B:70E (92±20 and 94±16MPa, respectively). Composites containing UDMA or Bis-EMA associated with Bis-GMA presented similar FM, statistically lower than 30B:35T:35U.
Tuesday, April 20th, 2010
Preparation and Evaluation of Dental Resin Luting Agents with Increasing Content of Bisphenol-A Ethoxylated Dimethacrylate
Rafael R. Moraes, Mário A.C. Sinhoreti, Lourenço Correr-Sobrinho, Fabrício A. Ogliari, Evandro Piva, and Cesar L. Petzhold
Journal of Biomaterials Applications, Jan 2010; vol. 24: pp. 453 – 473.
Abstract: Resin luting agents in which bisphenol-A glycidyl dimethacrylate (Bis-GMA) and/or triethylene glycol dimethacrylate (TEGDMA) are replaced with increasing amounts of bisphenol-A ethoxylated dimethacrylate are prepared. Degree of conversion (DC), diametral tensile strength (DTS), Young’s modulus (YM), Knoop hardness (KHN), film thickness (FT), water sorption (Wsp ), and solubility are evaluated. Regression analyses investigate the substitution of each monomer. The most appreciable differences are detected when TEGDMA is replaced: decreased DC, DTS, and Wsp, and increased YM, KHN, and FT. For substitution of Bis-GMA, the only significant differences are reduced Wsp and increased YM. An ideal formulation of resin cement would make use of the three monomers.
…Bis-GMA, TEGDMA, and/or Bis-EMA (Esstech Inc., Essington, PA, USA) were tested…photo-curable, 0.4 wt% of camphor- quinone (Esstech) and 0.8 wt% of N,N-dimethyl-p-toluidine…silanated strontium glass fillers (Esstech), 0.7 and 2 mm in size, to a constant…
This version was published on January 1, 2010.
Thursday, March 18th, 2010
Photobleaching of camphorquinone during polymerization of dimethacrylate-based resins
Silvana Asmusen, Gustavo Arenas, Wayne D. Cook, Claudia Vallo
Dental Materials, December 2009 (Vol. 25, Issue 12, Pages 1603-1611)
Abstract: Objective: The aim of this study was to compare the photobleaching rate of CQ in different dental resins. Methods: The photodecomposition rate of CQ/amine system in bis-GMA/TEGDMA, bis-EMA and UDMA polymerizing monomers was evaluated at different light intensities. The photobleaching of the CQ was studied by monitoring the decrease in light absorption as a function of continuous irradiation time. The absorption changes were assessed by recording the transmitted light that passed through samples of monomers containing CQ/amine. Results: Complete photobleaching of CQ was observed in all the monomer tested and the rate constant for the photobleaching was proportional to the radiation intensity. Hydrogen abstraction from amines by the excited CQ state via electron transfer and direct hydrogen abstraction from monomer structures were involved in the CQ photoreduction. CQ was photobleached in the absence of coinitiator in a dimethacrylate monomer containing a carbamate functional group (UDMA). This behavior was attributed to the presence of labile hydrogen atoms in the UDMA monomer. The CQ photobleaching rate constant in UDMA containing CQ/amine was similar to that in UDMA in the absence of amine. Moreover, the efficiency of CQ to photoinitiate the polymerization of UDMA in the absence of amine demonstrated that the radicals derived from the UDMA monomer via hydrogen abstraction are highly reactive toward double bonds.
Significance: CQ photoinitiates the polymerization of the UDMA monomer in the absence of amine and the efficiency of this process is comparable to that of traditional bis-GMA and bis-EMA monomers activated with CQ/amine.